金属学报(英文版)
Laser welding process of AZ61 magnesium alloys is investigated using a special CO2 laser experimental system. The effect of processing parameters including laser power, welding speed, and protection gas flow at the top and bottom is researched. The results show that an ideal weld bead can be formed by choosing the processing parameters properly. An optimized parameter range is obtained by a large number of experiments. Among them, laser power and welding speed are the two main parameters that determine the weld width and dimensions. The protect gas flow rate has a slight effect on the weld width, but it directly effects the surface color of the weld. The test results for typical welds indicate that the microhardness and tensile strength of the weld zone are better than that of the base metal. A fine-grained weld region has been observed and no obvious heat-affected zone is found. The weld zone mainly consists of small α-Mg phase, (α+ Al12Mg17), and other eutectic phases. The small grains and the eutectic phases in the joint are believed to play an important role in the increase of the strength of welds for AZ61 magnesium alloys.
关键词:
magnesium alloy
,
激光焊接
,
激光功率
,
焊接速度